    Stainless Steel

    Grade
    C (Max)
    Mn (Max)
    P (Max)
    S (Max)
    Si (Max)
    Cr
    Ni
    Mo
    Nitrogen (Max)
    Cu/ Others
    301
    0.15
    2.00
    0.045
    0.030
    1.00
    16.00 – 18.00
    6.00 – 8.00
    -
    0.10
    -
    304
    0.08
    2.00
    0.045
    0.030
    0.75
    18.00 – 20.00
    8.00- 10.50
    -
    0.10
    -
    304L
    0.030
    2.00
    0.045
    0.030
    0.75
    18.00 – 20.00
    8.00- 12.00
    -
    0.10
    -
    310S
    0.08
    2.00
    0.045
    0.030
    1.50
    24.00- 26.00
    19.00 – 22.00
    -
    -
    -
    316
    0.08
    2.00
    0.045
    0.030
    0.75
    16.00 – 18.00
    10.00 – 14.00
    2.00 – 3.00
    0.10
    -
    316L
    0.030
    2.00
    0.045
    0.030
    0.75
    16.00 – 18.00
    10.00 – 14.00
    2.00 – 3.00
    0.10
    -
    317
    0.08
    2.00
    0.045
    0.030
    0.75
    18.00 – 20.00
    11.00 – 14.00
    3.00 – 4.00
    0.10
    -
    317L
    0.030
    2.00
    0.045
    0.030
    0.75
    18.00 – 20.00
    11.00 – 15.00
    3.00 – 4.00
    0.10
    -
    321
    0.08
    2.00
    0.045
    0.030
    0.75
    17.00 – 19.00
    9.00 – 12.00
    -
    0.10
    Ti5 ( C + N ) Min or 0.70 max
    347
    0.08
    2.00
    0.045
    0.030
    0.75
    17.00 – 19.00
    9.00 – 13.00
    -
    -
    Cb= 10x ( C Min ) or 1.00 Max
    409
    0.08
    1.00
    0.040
    0.010
    1.00
    10.50 – 11.75
    0.50
    -
    -
    Ti= 6x (C+ N ) Min or 0.70 Max
    409M
    0.03
    0.81.2
    0.030
    0.030
    0.40.75
    11.00- 12.00
    1.5 max.
    -
    -
    Ti= 6x (C) Min or 0.70 Max
    410S
    0.08
    1.00
    0.040
    0.030
    1.00
    11.50- 13.50
    0.60
    -
    -
    -
    410
    0.15
    1.00
    0.040
    0.030
    1.00
    11.50- 13.50
    0.75
    -
    -
    -
    420
    0.35
    0.50
    0.035
    0.015
    0.50
    12.00 – 13.00
    0.20.3
    -
    -
    -
    430
    0.12
    1.00
    0.040
    0.030
    1.00
    16.00 – 18.00
    0.75
    -
    -
    -
    JSL AUS
    0.08
    7.08.0
    0.070
    0.030
    0.75
    15.50 – 16.50
    4.25 – 4.75
    -
    -
    0.9 – 1.10
    JS- 203
    0.08
    9.2510.25
    0.070
    0.030
    0.75
    14.25 – 15.25
    2.25 – 2.75
    -
    -
    1.60- 2.0
    301M
    0.10
    4.55.5
    0.060
    0.030
    0.75
    14.50 – 15.50
    6.0 – 7.0
    -
    -
    1.70- 1.90
    * Thickness of 1.27mm & below will have elongation of 20% min.

     

    Alloy Steel

    Chemical Composition,%

    Tensile Test

    Designation
    C max.
    Si
    P max
    S max
    Tensile Strength Kgf/mm2
    Yield Point Kgf/mm2,min.
    Elongation
    Test Piece
    %, min
    IS 2002-1
    0.18
    .010-0.35
    0.40
    0.40
    37-45
    55
    5.65/So
    4/So
    26
    30
    IS 2002-2A
    0.20
    0.10-0.35
    0.050
    0.050
    42-50
    50
    5.65/So
    4/So
    25
    29
    IS 2002-2b
    0.22
    0.10-0.35
    0.050
    0.050
    52-62
    50
    5.65/So
    4/So
    20
    24

     

    Kawasaki Specification [AG] Steel Plates for Galvanizing Pots

    Chemical Composition,%

    Tensile Test

    Bend test

    Designation
    C    Si    Mn     P   S
    Max       Max        Max
    Yield Point      Tensile Strength
    Kgf/mm2        Kgf/mm2.(N/mm2)
    Elongation
    %, Test Piece
    Angle of Bend
    Inside Radius
    AG
    0.09 tr.0.20-0.40 0.30 0.030
    –                           –
    –                  –

     

    ASTM A 285-78 Pressure Vessel Plates Carbon Steel, Low – and Intermediate- Tensile Strength

    Chemical Composition,%

    Tensile Test*1

    1. (i) Refer to  (1) for ASTM A 203

    (ii) Refer to (2) for ASTM A 203

    (iii) Refer to (4) for ASTM A 203.

    Designation
    C max
    Mn max
    P max
    S max
    Tensile Strength
    ksi (MPa),
    Yeild Strengh ksi(MPa),min.
    Elongation,% min

    GL=8 in.
    GL=2 in

    A 285 A
    0.17
    0.90
    0.035
    0.040
    45-65 (310-450)
    24(165)
    27              30
    A 285  B
    0.22
    0.90
    0.035
    0.040
    50-70(385-485)
    27(185)
    25
    28
    A 285 C
    0.28
    0.90
    0.035
    0.040
    55-75(380-515)
    30(205)
    23              27

     

    Stainless Steel

    Grade
    Tensile
    Strength Mpa, (Min)
    Yield
    Strength
    Mpa, (Min)
    %Age
    Elongation
    in 50mm
    gauge length min
    Hardness (Max)
    BHN
    Rb
    301
    515
    205
    40
    217
    95
    304
    515
    205
    40
    201
    92
    304L
    485
    170
    40
    201
    92
    310S
    515
    205
    40
    217
    95
    316
    515
    205
    40
    217
    95
    316L
    485
    170
    40
    217
    95
    317
    515
    205
    35
    217
    95
    317L
    515
    205
    40
    217
    95
    321
    515
    205
    40
    217
    95
    347
    515
    205
    40
    201
    92
    409
    380
    170
    20
    179
    88
    409M
    430
    275
    20
    187
    90
    410S
    415
    205
    22
    183
    89
    410
    450
    205
    20
    217
    89
    420
    700( max )
    -
    15
    217
    95
    430
    450
    205
    22
    183
    89
    JSL AUS
    515
    205
    40
    217
    95
    JS- 203
    515
    205
    40
    217
    95
    301M
    515
    205
    40
    217
    95

     

    Stainless Steel

    Grade
    Tensile
    Strength Mpa, (Min)
    Yield
    Strength
    Mpa, (Min)
    %Age
    Elongation
    in 50mm
    gauge length min
    Hardness (Max)
    BHN
    Rb
    301
    515
    205
    40
    217
    95
    304
    515
    205
    40
    201
    92
    304L
    485
    170
    40
    201
    92
    310S
    515
    205
    40
    217
    95
    316
    515
    205
    40
    217
    95
    316L
    485
    170
    40
    217
    95
    317
    515
    205
    35
    217
    95
    317L
    515
    205
    40
    217
    95
    321
    515
    205
    40
    217
    95
    347
    515
    205
    40
    201
    92
    409
    380
    170
    20
    179
    88
    409M
    430
    275
    20
    187
    90
    410S
    415
    205
    22
    183
    89
    410
    450
    205
    20
    217
    89
    420
    700( max )
    -
    15
    217
    95
    430
    450
    205
    22
    183
    89
    JSL AUS
    515
    205
    40
    217
    95
    JS- 203
    515
    205
    40
    217
    95
    301M
    515
    205
    40
    217
    95

     

    Alloy Steel

    Chemical Composition,%

    Tensile Test

    Designation
    C max.
    Si
    P max
    S max
    Tensile Strength Kgf/mm2
    Yield Point Kgf/mm2,min.
    Elongation
    Test Piece
    %, min
    IS 2002-1
    0.18
    .010-0.35
    0.40
    0.40
    37-45
    55
    5.65/So
    4/So
    26
    30
    IS 2002-2A
    0.20
    0.10-0.35
    0.050
    0.050
    42-50
    50
    5.65/So
    4/So
    25
    29
    IS 2002-2b
    0.22
    0.10-0.35
    0.050
    0.050
    52-62
    50
    5.65/So
    4/So
    20
    24